Effect of Alumina Addition to Zirconia Nano-composite on Low Temperature Degradation Process and Biaxial Strength | ||
Journal of Ultrafine Grained and Nanostructured Materials | ||
مقاله 8، دوره 49، شماره 2، اسفند 2016، صفحه 103-111 اصل مقاله (829.67 K) | ||
نوع مقاله: Research Paper | ||
شناسه دیجیتال (DOI): 10.7508/jufgnsm.2016.02.08 | ||
نویسندگان | ||
Moluk Aivazi* 1؛ Mohammadhossein Fathi1، 2؛ Farahnaz Nejatidanesh2؛ Vajihesadat Mortazavi3؛ Batoul Hashemibeni4 | ||
1Biomaterials Reserach Group, Department of Materials Engineering, Isfahan University of Technology, Isfahan, 84156-83111, Iran. | ||
2Dental Materials Research Center, School of Dentistry, Isfahan University of Medical Sciences, Isfahan,Iran. | ||
3Torabinejad Dental Research Center, Department of Operative Dentistry, School of Dentistry, Isfahan University of Medical Sciences, Isfahan 81746-73461, Iran. | ||
4Department of Anatomical Sciences and Molecular Biology, School of Medicine, Isfahan University of Medical Sciences, Isfahan 81746-73461, Iran. | ||
چکیده | ||
Ceramic dental materials have been considered as alternatives to metals for dental implants application. In this respect, zirconia tetragonal stabilized with %3 yttrium, is of great importance among the ceramic materials for endosseous dental implant application. Because of its good mechanical properties and color similar to tooth. The aim and novelty of this study was to design and prepare Y-TZP nano-composite to reduce the degradation process at low temperature by alumina addition and maintaining submicron grain sized. Also, flexural strength of nano-composite samples was evaluated. Toward this purpose, alumina-Y-TZP nano-composites containing 0–30 vol% alumina (denoted as A-Y-TZP 0-30) were fabricated using α-alumina and Y-TZP nano-sized by sintering pressure less method. The synthesized samples were characterized using x-ray diffraction, field emission scanning electron microscopy equipped with energy dispersive x-ray spectroscopy techniques. Nano-composite samples with high density (≥96%) and grain sized of ≤ 400 nm was obtained by sintering at 1270 °C for 170 min. After low temperature degradation test (LTD), A-Y-TZP20 and A-Y-TZP30 not showed monoclinic phase and the flexural strength in all of samples were higher than A-Y-TZP0. It was concluded that the grains were remained in submicron sized and A-Y-TZP20 and A-Y-TZP30 did not present biaxial strength reduction after LTD test. | ||
کلیدواژهها | ||
Alumina-zirconia nanocomposite؛ Low temperature degradation process؛ Endosseous dental implant؛ Y-TZP matrix | ||
مراجع | ||
1. Depprich R, Zipprich H, Ommerborn M, Naujoks C, Wiesmann HP, Kiattavorncharoen S, Lauer HC, Meyer U, Kübler NR, Handschel J. Osseointegration of zirconia implants compared with titanium: an in vivo study. Head & Face Medicine. 2008;4(1):1-8. 2. Manivasagam G, Dhinasekaran D, Rajamanickam A. Biomedical implants: Corrosion and its prevention-a review. Recent Patents on Corrosion Science. 2010;2(1):40-54. 3. Denry I, Kelly JR. State of the art of zirconia for dental applications. Dental Materials. 2008;24(3):299-307. 4. Gahlert M, Röhling S, Wieland M, Sprecher CM, Kniha H, Milz S. Osseointegration of zirconia and titanium dental implants: a histological and histomorphometrical study in the maxilla of pigs. Clinical Oral Implants Research. 2009;20(11):1247-53. 5. Al-Radha AS, Dymock D, Younes C, O’Sullivan D. Surface properties of titanium and zirconia dental implant materials and their effect on bacterial adhesion. Journal of Dentistry. 2012;40(2):146-53. 6. Chevalier J, Gremillard L, Deville S. Low-temperature degradation of zirconia and implications for biomedical implants. Annual Review of Materials Research. 2007;37:1-32. 7. Kelly JR, Denry I. Stabilized zirconia as a structural ceramic: an overview. Dental Materials. 2008;24(3):289-98. 8. Lughi V, Sergo V. Low temperature degradation-aging-of zirconia: A critical review of the relevant aspects in dentistry. Dental Materials. 2010;26(8):807-20. 9. Kanchana S. Zirconia a bio-inert implant material. IOSR Journal of Dental and Medical Sciences (IOSR-JDMS). 2013;1(12):66-7. 10. Rocchietta I, Fontana F, Addis A, Schupbach P, Simion M. Surface‐modified zirconia implants: tissue response in rabbits. Clinical Oral Implants Research. 2009;20(8):844-50. 11. Pirker W, Kocher A. Immediate, non-submerged, root-analogue zirconia implant in single tooth replacement. International Journal of Oral and Maxillofacial Surgery. 2008;37(3):293-5. 12. Stadlinger B, Hennig M, Eckelt U, Kuhlisch E, Mai R. Comparison of zirconia and titanium implants after a short healing period. A pilot study in minipigs. International Journal of Oral and Maxillofacial Surgery. 2010;39(6):585-92. 13. Tang D, Lim HB, Lee KJ, Lee CH, Cho WS. Evaluation of mechanical reliability of zirconia-toughened alumina composites for dental implants. Ceramics International. 2012;38(3):2429-36. 14. Storer RA. Annual Book of ASTM Standards: ASTM C373-88. Philadelphia. 1992:115. 15. Guazzato M, Albakry M, Swain MV, Ironside J. Mechanical properties of In-Ceram Alumina and In-Ceram Zirconia. International Journal of Prosthodontics. 2002;15(4):339-46. 16. International Standard Organization No.13356. Implants for surgery—Ceramic materials based on yttria-stabilized tetragonal zirconia (Y-TZP), 2008. 17. Hjerppe J. The Influence of Certain Processing Factors on the Durability of Yttrium Stabilized Zirconia Used As Dental Biomaterial. Turku: University of Turku; 2010. 18. Monshi A. A kinetic equation for diffusion-controlled dissolution of quartz spherical particles in glassy matrix of whitewares during firing. Interceram. 1998;47(3):155-62. 20. Chevalier J, Cales B, Drouin JM. Low‐Temperature Aging of Y‐TZP Ceramics. Journal of the American Ceramic Society. 1999;82(8):2150-4. 21. Chen CC, Hsiang HI, Zhou CM. Effects of the addition of minute amounts of alumina on the microstructure and sintering behavior of yttria stabilized tetragonal zirconia polycrystals ceramic via a co-precipitation process. Journal of Ceramic Processing Research. 2008;9(3):234-9. 22. Schmauder S, Schubert H. Significance of internal stresses for the martensitic transformation in Yttria‐stabilized tetragonal zirconia polycrystals during degradation. Journal of the American Ceramic Society. 1986;69(7):534-40. 23. Garvie RC, Nicholson PS. Phase analysis in zirconia systems. Journal of the American Ceramic Society. 1972;55(6):303-5. 24. Toraya H, Yoshimura M, Somiya S. Calibration Curve for Quantitative Analysis of the Monoclinic‐Tetragonal ZrO2 System by X‐Ray Diffraction. Journal of the American Ceramic Society. 1984;67(6):119-21. 25. Chevalier J, Deville S, Münch E, Jullian R, Lair F. Critical effect of cubic phase on aging in 3mol% yttria-stabilized zirconia ceramics for hip replacement prosthesis. Biomaterials. 2004;25(24):5539-45. 26. Borchers L, Stiesch M, Bach FW, Buhl JC, Hübsch C, Kellner T, Kohorst P, Jendras M. Influence of hydrothermal and mechanical conditions on the strength of zirconia. Acta biomaterialia. 2010;6(12):4547-52. 27. Kosmač T, Oblak Č, Marion L. The effects of dental grinding and sandblasting on ageing and fatigue behavior of dental zirconia (Y-TZP) ceramics. Journal of the European Ceramic Society. 2008;28(5):1085-90. 28. Ban S, Sato H, Suehiro Y, Nakanishi H, Nawa M. Biaxial flexure strength and low temperature degradation of Ce‐TZP/Al2O3 nanocomposite and Y‐TZP as dental restoratives. Journal of Biomedical Materials Research Part B: Applied Biomaterials. 2008;87(2):492-8. 29. Cattani-Lorente M, Scherrer SS, Ammann P, Jobin M, Wiskott HA. Low temperature degradation of a Y-TZP dental ceramic. Acta Biomaterialia. 2011;7(2):858-65. 30. Xu J, Tang D, Lee KJ, Lim HB, Park K, Cho WS. Comparison of fracture toughness evaluating methods in 3Y-TZP ceramics reinforced with Al2O3 particles. Journal of Ceramic Processing Research. 2012;13(6):683-7. 31. Lange FF. Transformation toughening. Journal of Materials Science. 1982;17(1):225-34. 32. Swab JJ, Stowell SC. Properties of a TAP/Al2O3 composite after long-term exposure at 1000 deg C. Final report. Army Materials Research Agency, Watertown, MA (United States). Materials Technology Lab.; 1991. | ||