Structural Characterization and Ordering Transformation of Mechanically Alloyed Nanocrystalline Fe-28Al Powder
|Journal of Ultrafine Grained and Nanostructured Materials|
|مقاله 9، دوره 49، شماره 2، اسفند 2016، صفحه 112-119 اصل مقاله (1.6 M)|
|نوع مقاله: Research Paper|
|شناسه دیجیتال (DOI): 10.7508/jufgnsm.2016.02.09|
|Lima Amiri Talischi؛ Ahad Samadi*|
|Department of Materials Engineering, Sahand University of Technology, P.O.Box 51335-1996, Tabriz, Iran.|
|The synthesis of nanocrystalline Fe3Al powder by mechanical alloying as well as the structural ordering of the synthesized Fe3Al particles during the subsequent thermal analysis were investigated. Mechanical alloying was performed up to 100 hours using a planetary ball mill apparatus with rotational speed of 300 rpm under argon atmosphere at ambient temperature. The synthesized powders were characterized using X-ray diffraction, SEM observations and differential scanning calorimetry (DSC). The results show that the A2-type Fe3Al with disordered bcc structure is only formed after 70 hours milling. The corresponding lattice strain, mean crystallite and particle sizes for the 70 hours milled Fe3Al powder were determined as 2.5%, 10 and 500 nm, respectively. The subsequent heating during DSC causes a DO3-type Fe3Al ordering in 70 and 100 hours milled powders, however in 40 hours milled powder it only assists for the formation of disordered solid solution. Longer milling time induces a large amount of lattice strain in Fe3Al powder particles and consequently facilitates the atomic diffusion thus decreases the activation energy of ordering. The activation energy for ordering transformation of 100 hours Fe3Al milled powder was calculated as 152.1 kJ/mole which is about 4 kJ/mole lower than that for 70 hours milled powder.|
|Fe3Al intermetallic compound؛ Mechanical alloying؛ Nanocrystalline powder؛ X-ray diffraction, Ordering|
1. Sauthoff G. Iron Aluminides and Related Phases. Intermetallics. VCH Verlagsgesellschaft mbH. Weinheim. 1995.
2. Westbrook JH, Fleischer RL. Intermetallic Compounds. Structural Applications of Intermetallic Compounds. John Wiley. 1991.
3. Morris DG, Munoz-Morris MA, Baudin C. The high-temperature strength of some Fe3Al alloys. Acta Materialia. 2004;52(9):2827-36.
4. Itoi T, Mineta S, Kimura H, Yoshimi K, Hirohashi M. Fabrication and wear properties of Fe3Al-based composites. Intermetallics. 2010;18(11):2169-77.
5. Li YF, La PQ, Wei YP, Yang LU, Yang YA. Effect of Hot Pressing on Microstructure and Mechanical Properties of Bulk Nanocrystalline Fe3Al Materials Containing Manganese Element. Journal of Iron and Steel Research, International. 2011;18(3):65-71.
6. McKamey CG, Liu CT. Chromium addition and environmental embrittlement in Fe3Al. Scripta Metallurgica et Materialia. 1990;24(11):2119-22.
7. Zamanzade M, Vehoff H, Barnoush A. Cr effect on hydrogen embrittlement of Fe3Al-based iron aluminide intermetallics: Surface or bulk effect. Acta Materialia. 2014;69:210-23.
8. Stoloff NS, Liu CT. Environmental embrittlement of iron aluminides. Intermetallics. 1994;2(2):75-87.
9. Oleszak D, Shingu PH. Mechanical alloying in the Fe-Al system. Materials Science and Engineering: A. 1994;181:1217-21.
10. Enayati MH, Salehi M. Formation mechanism of Fe3Al and FeAl intermetallic compounds during mechanical alloying. Journal of Materials Science. 2005;40(15):3933-8.
11. Wang J, Xing J, Qiu Z, Zhi X, Cao L. Effect of fabrication methods on microstructure and mechanical properties of Fe3Al-based alloys. Journal of Alloys and Compounds. 2009;488(1):117-22.
12. Peng LM, Li H, Wang JH, Gong M. High strength and high fracture toughness ceramic−iron aluminide (Fe3Al) composites. Materials Letters. 2006;60(7):883-7.
13. Davis JR. Vol 9: Metallography and Microstructures. ASM International, Materials Park, OH. 2004.
14. Bonetti E, Scipione G, Valdre G, Enzo S, Frattini R, Macri PP. A study of nanocrystalline iron and aluminium metals and Fe3Al intermetallic by mechanical alloying. Journal of Materials Science. 1995;30(9):2220-6.
15. Farrokhi A, Samadi A, Asadi Asadabad M, Amiri Talischi L. Characterization of mechanically alloyed nano structured Fe3Al intermetallic compound by X-ray diffractometry. Advanced Powder Technology. 2015;26(3):797-801.
16. Suryanarayana C. Mechanical alloying and milling. Progress in Materials Science. 2001;46(1):1-84.
17. Cullity BD. Elements of X-Ray Diffraction 2nd edition. Addision-Wesley Pub. Co. Inc. 1978.
18. Guinebretière R. X-ray diffraction by polycrystalline materials. John Wiley & Sons. 2013.
19. Kissinger HE. Variation of peak temperature with heating rate in differential thermal analysis. Journal of Research of the National Bureau of Standards. 1956;57(4):217-21.
20. Cahn RW. Lattice parameter changes on disordering intermetallics. Intermetallics. 1999;7(10):1089-94.
21. Karimbeigi A, Zakeri A, Sadighzadeh A. Effect of composition and milling time on the synthesis of nanostructured Ni-Cu alloys by mechanical alloying method. Iranian Journal of Materials Science & Engineering. 2013;10(3):27-31.
22. Rafiei M, Enayati MH, Karimzadeh F. The effect of Ti addition on alloying and formation of nanocrystalline structure in Fe–Al system. Journal of Materials Science. 2010;45(15):4058-62.
23. Haghighi SE, Janghorban K, Izadi S. Structural evolution of Fe–50at.% Al powders during mechanical alloying and subsequent annealing processes. Journal of Alloys and Compounds. 2010;495(1):260-4.
24. Zhu SM, Iwasaki K. Characterization of mechanically alloyed ternary Fe–Ti–Al powders. Materials Science and Engineering: A. 1999;270(2):170-7.
25. Wang J, Xing JD, Tang HP, Yang BJ, Li YN. Microstructure and mechanical properties of Fe3Al alloys prepared by MA-PAS and MA-HP. Transactions of Nonferrous Metals Society of China. 2011;21(11):2408-14.
26. Guilemany JM, Cinca N, Casas L, Molins E. Ordering and disordering processes in MA and MM intermetallic iron aluminide powders. Journal of Materials Science. 2009;44(8):2152-61.
27. Feder R, Cahn RW. Kinetics of ordering in Fe3Al. Philosophical Magazine. 1960;5(52):343-53.